Metal cored wire for joining and repair of AISI 4130 without a quench and temper, only stress relief. Ni > 1% and hardness Vickers < 250 for NACE MR0175 adherence.

Low alloy submerged arc wire for joining and repair of AISI 4130, 8630, 8630 modified and Q&T steels that require PWHT.  High strength and low temperature toughness after extended PWHT.

High strength and low-temp toughness SAW wire for high strength steels requiring stress relief.

Ultra high strength, low alloy composite GMAW wire recommended for the joining and repair of HSLA steels with similar recorded strength levels, such as ASTM A148, A643, A757, HY130, LQ130 and Weldox 960 steels.

Ultra high strength, low alloy composite wire recommended for the joining and repair of HSLA steels with similar recorded strength levels, such as ASTM A148, A643, A757, HY130, LQ130 and Weldox 960 steels.

Metal-cored cut length wire for manual TIG welding. HSLA for join and repair of AISI 4340 and similar forgings without re-quench and temper.

A high strength, low alloy SAW wire recommended for joining AISI 4130, 8630 and variations thereof. This wire was specifically designed for welding Q&T steels that will undergo PWHT. Combined with appropriate flux will yield 100ksi UTS, 100 avg ft-lb at -20F, while still adhering to NACE MR0175

Low alloy Cr-Mo metal cored wire for 2.25% Cr – 1% Mo steels, such as ASTM A327 Gr. 22, and for joining dissimilar combinations of Cr-Mo and carbon steels.

Low alloy Mn-Mo metal cored wire for welding high strength low alloy steels, such as ASTM A302 Gr. B, and repair of Mn-Mo castings, such as ASTM A49, A291 and A735.

Low alloy submerged arc welding wire for joining and repair of AISI 4130, 8630, 8630 modified and quenched and tempered steels that will undergo PWHT. Nickel < 1% and hardness < 23 HRc for NACE MR0175 adherence.